10005
10005 is an unsupported single-sided acrylic transfer tape built on a high-performance, solvent-free acrylic dispersion adhesive with a total thickness of 0.04–0.06 mm (approximately 1.6–2.4 mils). The adhesive provides balanced peel adhesion and shear performance on polar and smooth substrates, reaching 22 N/25mm peel on steel after 24 hours. The tape is rated for service from −22°F to 248°F.
Key Properties
- Peel Adhesion to Steel, 24-hour Dwell @ 73°F: 22 N/25mm
- Peel Adhesion to Glass, 24-hour Dwell @ 73°F: 20 N/25mm
- Static Shear @ 73°F, Test After 1 Hour: 500 g/2 mm
- Temperature Resistance: −22°F to 248°F
- Liner: Yellow silicone-coated paper
- Total Thickness Without Liner: 0.04–0.06 mm (~1.6–2.4 mils)
We want to help!
Enter your information and we'll get you in touch with our knowledgable staff. We know how important to the right product for your project.
Request a Consultation
- Specifications
- Applications
- General Info
- FAQs
Specifications
Physical Properties
| Property | Value | Test Method |
| Total Thickness Without Liner | 0.04–0.06 mm | — |
| Adhesive Type | Acrylic Dispersion | — |
| Adhesive System | Permanent Adhesive | — |
| Adhesive Side | Single Sided Adhesive | — |
| Color | Clear | — |
| Liner | Yellow silicone-coated paper | — |
Adhesion Properties
| Property | Value | Test Method |
| Peel Adhesion to Aluminum, Powder-Coated @ 73°F, Test After 1 Minute | 16 N/25mm | — |
| Peel Adhesion to Glass @ 73°F, Test After 1 Minute | 18 N/25mm | — |
| Peel Adhesion to Glass @ 73°F, Test After 10 Minutes | 19 N/25mm | — |
| Peel Adhesion to Glass @ 73°F, Test After 24 Hours | 20 N/25mm | — |
| Peel Adhesion to PP @ 73°F, Test After 1 Minute | 4 N/25mm | — |
| Peel Adhesion to Steel @ 73°F, Test After 1 Minute | 18 N/25mm | — |
| Peel Adhesion to Steel @ 73°F, Test After 10 Minutes | 21 N/25mm | — |
| Peel Adhesion to Steel @ 73°F, Test After 24 Hours | 22 N/25mm | — |
| Shear Adhesion Failure Temperature, Test After 1 Hour, 1.8°F/Minimum Temperature Increase | 248°F | — |
| Static Shear @ 73°F, Test After 1 Hour | 500 g/2 mm | — |
| Tack | High | — |
Peel adhesion test performed with a 23µm PET carrier, 180° peel angle, 300 mm/min peel speed and 25 mm tape width. Shear adhesion test performed with a 23µm PET carrier and 625 mm² shear area. SAFT test performed with a 23µm PET carrier, 40 g/m² adhesive coating weight and 625 mm² shear area.
Thermal Properties
| Property | Value | Test Method |
| Temperature Resistance | −22°F to 248°F | — |
| Recommended Processing Temperature | 50°F to 86°F | — |
Environmental Performance
| Property | Value | Test Method |
| Aging Resistance | High | — |
| Condensation Water Resistance | Limited | — |
| Plasticizer Resistance | Limited | — |
- Laminating and bonding of metal, wood, foam, plastic, paper, and cardboard components
- Permanent adhesive bonding on polar substrates including glass, steel, and powder-coated aluminum
- Lamination of smooth and slightly textured surfaces where full-surface adhesive transfer is required
- Solvent-free adhesive mounting in applications where VOC-free construction is required
- General-purpose converting for graphics, display, and paper-to-substrate bonding applications
Common industries: Graphic arts, display and signage, paper converting, industrial manufacturing, packaging.
10005 is an unsupported acrylic transfer tape coated from a solvent-free acrylic dispersion. Without a carrier, the entire tape consists of adhesive mass delivered on a yellow silicone-coated paper release liner, making it suitable for laminating and bonding applications where full-surface adhesive contact is required.
The adhesive is formulated with balanced initial tack and well-matched peel and shear properties, making it appropriate for polar substrates and smooth or slightly textured surfaces including metal, glass, wood, foam, plastics, paper, and cardboard.
Peel adhesion on steel builds from 18 N/25mm at 1 minute to 22 N/25mm after 24 hours, and on glass from 18 N/25mm to 20 N/25mm over the same dwell period — indicating typical pressure-sensitive adhesive build behavior on polar surfaces. Peel adhesion to polypropylene is 4 N/25mm at 1 minute, confirming that the adhesive is optimized for polar substrates rather than low surface energy materials.
The tape offers high aging resistance and high tack, but condensation water resistance and plasticizer resistance are both rated as Limited. Shear Adhesion Failure Temperature (SAFT) is 248°F. Recommended processing temperature is 50°F to 86°F.
What differentiates 10005 from carrier-supported transfer tapes?
10005 is an unsupported acrylic transfer tape — 100% adhesive mass with no scrim, film, or foam carrier. This allows the tape to be fully consumed into the bond line for direct substrate-to-substrate lamination and provides more compliant contact on smooth surfaces. The trade-off is lower dimensional stability during handling compared to scrim-reinforced or carrier-supported transfer tapes.
Why is peel adhesion important for this transfer tape?
For unsupported transfer tapes, peel adhesion measures the core functional performance of the adhesive against the substrate — there is no carrier to contribute mechanical strength. The 10005 TDS reports substrate-specific peel values at 1-minute, 10-minute, and 24-hour dwell times, allowing specifiers to see how bond strength builds over time on glass (18→20 N/25mm) and steel (18→22 N/25mm). The 4 N/25mm value on polypropylene confirms this adhesive is optimized for polar surfaces, not LSE substrates.
What is the operating temperature range for 10005?
10005 has a temperature resistance range of −22°F to 248°F, with a recommended processing (application) temperature of 50°F to 86°F.
Is 10005 suitable for moisture-exposed or plasticizer-containing environments?
The TDS rates aging resistance as High, but condensation water resistance and plasticizer resistance are both rated as Limited. 10005 is not the recommended selection for applications involving prolonged moisture exposure or bonding to highly plasticized vinyl substrates. No specific regulatory compliance standards are listed on the TDS for this material.
How should 10005 be specified?
Specify grade (10005), thickness (0.04–0.06 mm), target substrate, compliance requirements, dimensional tolerances, and finished format.