6113-10 PTFE Film Tape
6113-10 is a single-coated PTFE film tape constructed with a 0.010″ skived virgin PTFE film carrier and 0.002″ of acrylic adhesive, for a 0.012″ total nominal thickness. The skived virgin PTFE provides a very low coefficient of friction with chemical resistance and conformability, supporting applications including wear stripping, lining, chemical-resistant surface protection, and shrink wrap thermal tape. Peel adhesion is 70 oz typical (55 oz minimum) per ASTM D3330 Method A. Operating temperature range is −40°F to 350°F.
Key Properties
- Peel Adhesion (Typical): 70 oz (ASTM D3330 Method A)
- Peel Adhesion (Minimum): 55 oz (ASTM D3330 Method A)
- Operating Temperature: −40°F to 350°F
- Substrate Thickness: 0.010″ PTFE film (nominal)
- Adhesive Thickness: 0.002″ acrylic (nominal)
- Overall Thickness: 0.012″ (nominal)
We want to help!
Enter your information and we'll get you in touch with our knowledgable staff. We know how important to the right product for your project.
Request a Consultation
- Specifications
- Applications
- General Info
- FAQs
Physical Properties
| Property | Value | Test Method |
| Overall Thickness (Nominal) | 0.012″ | ASTM D3652 |
| Substrate Thickness (Nominal) | 0.010″ | ASTM D3652 |
| Adhesive Thickness (Nominal) | 0.002″ | ASTM D3652 |
| Color | Blue | — |
| Material / Substrate | PTFE film | — |
| Adhesive System | Permanent Adhesive | — |
| Adhesive Side | Single Sided Adhesive | — |
| Adhesive Type | Acrylic | — |
Adhesion Properties
| Property | Value | Test Method |
| Peel Adhesion (Typical) | 70 oz | ASTM D3330 Method A |
| Peel Adhesion (Minimum) | 55 oz | ASTM D3330 Method A |
Thermal Properties
| Property | Value | Test Method |
| Operating Temperature | −40°F to 350°F | — |
Shelf Life / Storage
| Property | Value | Test Method |
| Adhesive Shelf Life | 24 months | — |
- Wear stripping where two surfaces must slide against each other with minimal friction and wear
- Lining of chutes, slides, and material-handling surfaces where low-friction flow is required
- Chemical-resistant surface protection in process and industrial environments
- Shrink wrap thermal tape applications requiring high-temperature PTFE surface stability
- Industrial wear-surface and friction-management converting where PTFE properties are required
Common industries: Industrial manufacturing, material handling, packaging machinery, chemical processing, plastics fabrication.
6113-10 PTFE Film Tape is a single-coated tape constructed with a 0.010″ (10 mil) skived virgin PTFE film carrier coated with 0.002″ of acrylic adhesive, for a 0.012″ overall nominal thickness. The PTFE substrate is supplied in blue. PTFE (polytetrafluoroethylene) provides three defining material properties that drive the tape’s primary applications: very low coefficient of friction, broad chemical resistance, and high-temperature stability.
The skived virgin PTFE designation refers to the manufacturing method — PTFE billet is mechanically skived (peeled) into a thin film rather than extruded, producing a fully fluorinated, virgin polymer film with consistent thickness and surface characteristics.
Typical applications leverage the low-friction PTFE surface: wear stripping where two surfaces must slide against each other with minimal friction or wear; lining of chutes, slides, and conveyors where material flow is impeded by friction; chemical-resistant surface protection in process environments; and shrink wrap thermal tape applications. Performance characteristics include very good conformability for a fluoropolymer film.
Peel adhesion is 70 oz typical with a 55 oz minimum specification per ASTM D3330 Method A. Operating temperature spans −40°F to 350°F. Adhesive shelf life is 24 months.
What differentiates 6113-10 PTFE Film Tape from other film tapes?
The PTFE film carrier is the defining differentiator. PTFE provides three properties that no other thermoplastic film carrier matches simultaneously: very low coefficient of friction, broad chemical resistance, and high-temperature stability to 350°F. Skived virgin PTFE specifically delivers consistent thickness and full polymer purity, supporting applications where the surface properties must be predictable and unmodified. Standard polyester or polyethylene-backed tapes cannot replicate any of these characteristics.
Why is peel adhesion important when selecting this tape?
For PTFE film tape, peel adhesion measures the bond between the acrylic adhesive and the substrate, since the PTFE itself is non-adhesive. The 70 oz typical / 55 oz minimum range per ASTM D3330 Method A reflects the moderate but reliable adhesion expected from acrylic systems. The TDS reports a typical/minimum peel adhesion specification — useful for QC and incoming inspection planning.
What is the operating temperature range for 6113-10?
6113-10 has an operating temperature range of −40°F to 350°F.
Is 6113-10 suitable for chemical-exposed or low-friction wear applications?
Yes. The TDS explicitly identifies wear stripping, chemical resistance, lining, and shrink wrap thermal tape as primary applications. PTFE's broad chemical resistance and very low coefficient of friction make this tape the standard selection for those use cases. No specific regulatory compliance standards are listed on the TDS for this material.
How should 6113-10 be specified?
Specify product (6113-10 PTFE Film Tape), substrate thickness (0.010" PTFE film), adhesive thickness (0.002" acrylic), overall thickness (0.012"), color (Blue), application category (wear stripping, lining, chemical resistance, or thermal tape), compliance requirements, dimensional tolerances, and finished format.